OPNYL OP66GF33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xvak07_OPNYL-OP66GF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.38 | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | 0.20 to 0.30 | % | ASTM D955 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1 | 8500 | 7000 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 170 | 125 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.5 | 4.2 | % | ASTM D638 |
| Flexural Modulus 4 | 9000 | 7800 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 210 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Annealed, 3.20 mm | 252 | -- | °C | |
| 1.8 MPa, Annealed, 3.20 mm | 246 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0320GN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Badaflex® TPE-S 40D 1038 | Bada AG | SEBS | Badaflex® |
| Boda BDF-LB2752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Dryflex® 502400S | ELASTO | SEBS | Dryflex® |
| LNP™ LUBRICOMP™ LCL36 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |