Evoprene™ G 3292
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AlphaGary |
| Trademark: | Evoprene™ G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XuFqbM_Evoprene-G-3292.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A very wide range of Evoprene™ G compounds is available for applications in all sectors of industry. The range is based on the widely specified SEBS (styrene - ethylene butylene - styrene) and related hydrogenated block copolymers. These polymers are fully saturated, i.e. there are no double bonds present so the resistance to oxidation, ozone and general outdoor weathering is excellent. For extended outdoor use, however, it is important to ensure additional UV stabilization is specified, especially in light colours. Evoprene™ G grades are used in service over a wide temperature range (see notes below) but each component should be fully assessed for temperature resistance before being put into service. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 2782 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 37 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.800 | MPa | ISO 37 |
| Tensile Stress (Yield) | 6.10 | MPa | ISO 37 |
| Tensile Elongation (Break) | 620 | % | ISO 37 |
| Tear Strength 1 | 18 | kN/m | ISO 34-1 |
| Compression Set (22°C, 72 hr) | 39 | % | ISO 815 |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | |
| Electric Strength | 24 to 28 | kV/mm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| M-S Flow | 1.57 | MPa | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 170 to 190 | °C | |
| Front Temperature | 170 to 190 | °C | |
| Nozzle Temperature | 170 to 190 | °C | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Fast | ||
| Vent Depth | 0.020 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badaprene® TPV 35A 1005 | Bada AG | PP+EPDM | Badaprene® |
| HAIPLEN H30 G6 BA X0 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Kpren 130B | Shandong Xuye New Materials Co., Ltd. | CM | Kpren |
| LEXAN™ PC1800R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| MAJORIS GC321 | AD majoris | PP, Unspecified | MAJORIS |