TECHNYL® B 230 GREY 1429 H
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XuFW5P_TECHNYL-B-230-GREY-1429-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® B 230 Grey 1429 H is an unfilled copolyamide 6.6/6, impact modified, for injection molding. The product is available in grey color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 2.1 | -- | % | |
| Flow | 2.2 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.4 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.07 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2300 | 900 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield | 65.0 | -- | MPa | ASTM D638 |
| Yield | 60.0 | 45.0 | MPa | ISO 527-2/1A |
| Break | 50.0 | 40.0 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 70 | -- | % | ASTM D638 |
| Break | 50 | 250 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 2400 | -- | MPa | ASTM D790 |
| -- | 2000 | 700 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 85.0 | -- | MPa | ASTM D790 |
| -- | 80.0 | 27.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C | 140 | -- | J/m | ASTM D256 |
| 23°C | 7.0 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 185 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | 16 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.070 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 475 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 255 to 265 | °C | |
| Front Temperature | 265 to 275 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8860 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TAIRIPRO T1202 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Ebalta GM 956 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| LG PVC LS130S | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| Plaslube® PA6/6 GF30 TL15 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |