PRL NY66-G13-(color)H is a Polyamide 66 (Nylon 66) product filled with 13% glass fiber. It can be processed by injection molding and is available in North America.

Characteristics include:
  • RoHS Compliant
  • Heat Stabilizer
  • Lubricated
General Information
Filler / Reinforcement
  • Glass Fiber, 13% Filler by Weight
Additive
  • Heat Stabilizer
  • Lubricant
Features
  • Heat Stabilized
  • Lubricated
RoHS Compliance
  • RoHS Compliant
Forms
  • Pellets
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.22g/cm³ASTM D792
Molding Shrinkage - Flow 0.40 to 0.60%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Strength ASTM D638
    Yield, 3.18 mm 110MPa
    Break, 3.18 mm 110MPa
Flexural Modulus (3.18 mm)4720MPaASTM D790
Flexural Strength (3.18 mm)159MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.18 mm)64J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, Unannealed, 3.18 mm 249°C
    1.8 MPa, Unannealed, 3.18 mm 241°C
InjectionNominal ValueUnit
Drying Temperature 73.9 to 85.0°C
Drying Time 3.0 to 4.0hr
Drying Time, Maximum 8.0hr
Rear Temperature 271 to 282°C
Middle Temperature 277 to 288°C
Front Temperature 293 to 304°C
Processing (Melt) Temp 288 to 299°C
Mold Temperature 65.6 to 104°C
Resin Grade Manufacturer Category Trademark
PRL NY6-G43-(color)H Polymer Resources Ltd. Nylon 6 PRL
Rotec® ASA T 115 ROMIRA GmbH ASA Rotec® ASA
Adell PP EA-34 Adell Plastics, Inc. PP Homopolymer Adell PP
Elastron® G G200.A70.N Elastron USA, Inc. SEBS Elastron® G
Sylvin 5143-88 White 1318 Sylvin Technologies Incorporated PVC, Unspecified Sylvin