RTV-2 GI-650
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XtdUkh_RTV-2-GI-650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GI-650 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-650 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can be accelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-650 is extremely useful for those applications where superior mechanical properties are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | |
| Shrinkage - Cured | 0.10 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 171 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.932 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 11 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 20000 to 30000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Blue | ||
| -- 3 | White | ||
| Viscosity | |||
| -- 4 | 0.30 to 0.40 | Pa·s | |
| -- 5 | 40 to 60 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 90 to 150 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 6 | 19 to 27 | ||
| Shore A 7 | 23 to 31 | ||
| Tensile Strength | 3.28 to 3.62 | MPa | ASTM D412 |
| Tensile Elongation at Break | 300 to 350 | % | ASTM D412 |
| Tear Strength | 15.8 to 19.3 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Activator |
| 5 . | Base |
| 6 . | 1 Day |
| 7 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP462S | LyondellBasell Industries | PP Homopolymer | Moplen |
| APEX® 3301-65NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Flontech® FT-1-8 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KumhoSunny PC/ABS HAC8260H | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| POLIMAXX 2300NC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |