LNP™ LUBRILOY™ RF206AXH compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xtcuqv_LNP-LUBRILOY-RF206AXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* RF206AXH is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material include: Wear Resistant, Healthcare. Also known as: LNP* LUBRILOY* Compound RF-30 HC Product reorder name: RF206AXH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 | % | |
| Across Flow : 24 hr | 1.2 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.38 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.66 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8770 | MPa | ASTM D638 |
| -- | 8470 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 121 | MPa | ASTM D638 |
| Break | 118 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.5 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7060 | MPa | ASTM D790 |
| -- 5 | 7200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 167 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 173 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.40 | ||
| vs. Itself - Static | 0.40 | ||
| Wear Factor - Washer | 45.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 7 | 9.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D4812 |
| 23°C 8 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.3 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 258 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 252 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 241 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 224 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 271 to 282 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GLS PP YT06 (PP30 Talc) | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| LUVOCOM® 1105/GF/30/BK-1-LB | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Polimid B 34 | Poliblend S.p.a. | Nylon 6 | Polimid B |
| Sylvin 83013-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RTP 699 X 141354 | RTP Company | ABS | RTP |