HANWHA LDPE 5321 (Film)
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XsDUly_HANWHA-LDPE-5321-Film-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LDPE 5321 is manufactured by DOW tubular high pressure process and designed for variety of film application such as general package film. LDPE 5321 has well balanced property of high clarity, mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 22.1 | MPa | ASTM D882 |
| TD : Break, 30 µm | 16.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 320 | % | ASTM D882 |
| TD : Break, 30 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 80 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 88.3 | kN/m | ASTM D1004 |
| TD : 30.0 µm | 83.4 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 |
| Melting Temperature | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 6.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 - 170 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.025 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene CFN3088 | Teknor Apex Asia Pacific PTE. LTD. | LDPE+LLDPE | Sinpolene |
| Nypol® PA A3 G10 N8 NTLA014 NR386 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Beetle® PBTS800 | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| Hanwha Total PP SI73 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hylon® N1200HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |