Next Nylon 6 Prime Series NGF25-01BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XrnGiv_Next-Nylon-6-Prime-Series-NGF25-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass Fiber Reinforced FR Black compound Product Applications Industrial controls and Electrical insulation system Benefits This Red Phosphorous Flame retardent grade provides robust UL-94 VO, While offering good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.1 | -- | % | ASTM D955 |
| Transverse flow | 0.52 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.7 | -- | % | ASTM D570 |
| Saturation 1 | 6.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 95 | -- | ASTM D785 | |
| Class r | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 120 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | 7500 | -- | MPa | ASTM D790 |
| Flexural Strength | 210 | 180 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 210 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 185 | -- | °C | ASTM D648 |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | 24 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 350 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Possibles formation of phosphates in humid warm enviornments. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 TFE 15 Z | RTP Company | PP, Unspecified | RTP |
| SUMIKASUPER® LCP E5008 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Vydyne® R533 BK0661 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Bormed™ HG820MO | Borealis AG | PP Homopolymer | Bormed™ |
| COPEC® CC6FDN (Series: VS/MR/AD1) | KRAIBURG TPE | TPE | COPEC® |