Order Products : sales@su-jiao.com
ASTAMID™ MA3LK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xqca5s_ASTAMID-MA3LK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MA3LK is an impact toughened, heat stabilised Polyamide 66 grade designed for use in long flow path components requireing additional toughness and resistance to heat ageing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.09 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 73.0 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 75 | 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2400 | 1000 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 250 | 500 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 59.0 | -- | °C | ASTM D648 |
| CLTE - Flow | 8.0E-4 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 130 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time (Opened Bag): >12 hr |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borlink™ LE0516 | Borealis AG | PE, Unspecified | Borlink™ |
| BMC 501 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Hoffman PVC V0-072x1 CLEAR | Hoffman Plastic Compounds Inc. | PVC, Flexible | Hoffman PVC |
| Hylon® N1000TL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LEXAN™ VR2920 resin | SABIC Innovative Plastics | PC | LEXAN™ |