Durethan® BKV 15 H2.0 DUS008 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XpG2MI_Durethan-BKV-15-H2-0-DUS008-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 15 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.80 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.20 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.50 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6600 | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 120 | 59.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.4 | 12 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5700 | 2800 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% Strain | 175 | 75.0 | MPa | ISO 178/A |
| 23°C | 195 | 100 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 4.8 | 7.3 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-070, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 2.00 | -- | J | |
| -- 9 | 2.20 | -- | J | |
| Film Puncture Force | ISO 6603-2 | |||
| -- 10 | 546 | -- | N | |
| -- 11 | 574 | -- | N |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 35 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | < 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 35 | 40 | kJ/m² | |
| 23°C | 40 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 216 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature 12 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam BFR330A | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| VALOX™ 508 resin | SABIC Innovative Plastics | PC+PBT | VALOX™ |
| Bergadur™ PBT-GL30 BK007 | PolyOne Corporation | PBT | Bergadur™ |
| Borealis PP SR533 | Borealis AG | PP, Unspecified | Borealis PP |
| INCOLOR TPE45AOM | Infinity LTL Engineered Compounds | TPU, Unspecified | INCOLOR |