VITAMIDE® AR35BK8502
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xolsmh_VITAMIDE-AR35BK8502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AR35BK8502 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 0.60 to 0.90 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 150 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 220 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 240 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 22 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 154 HF | RTP Company | PP, Unspecified | RTP |
| RTV-2 GI-184B/GI-1000A | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Royalene® 645 | Lion Copolymer, LLC | EPDM | Royalene® |
| Delta ABR-1G30/1 | Delta Polymers | ABS | Delta |
| Gallonprene® GP520-9011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |