CYROLITE® Med 2
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | CYROLITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XogYf7_CYROLITE-Med-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CYROLITE Med 2 compound is an impact-modified acrylic-based multipolymer for molding and extrusion of medical applications. Typical properties of CYROLITE® acrylic-based multipolymer compounds are:
The special properties of CYROLITE Med 2 compound are:
Used for injection molding and extrusion of medical devices. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 2.1 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.38 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 33 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1720 | MPa | ASTM D638 |
| Tensile Strength | 36.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.9 | % | |
| Break | 22 | % | |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Flexural Strength | 59.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 72.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 |
| CLTE - Flow (0 to 156°C) | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 85.0 | % | ASTM D1003 |
| Haze (3200 µm) | 7.0 | % | ASTM D1003 |
| Yellowness Index (3.20 mm) | -1.0 | YI | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 216 to 249 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinylbond 95-950-55 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Chemisat® LCH-7302X | Zeon Chemicals L.P. | NBR | Chemisat® |
| DENYL 66 1510 | Vamp Tech | Nylon 66 | DENYL |
| Globalene® 7633 | Lee Chang Yung Chemical Industry Corp. | PP Impact Copolymer | Globalene® |
| Hifax CA 7271 A | LyondellBasell Industries | TPO (POE) | Hifax |