MAJORIS DFR210
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xo8trw_MAJORIS-DFR210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR210 is a halogen free flame retardant compound with glass fiber reinforced UL 94 VO , intended for injection moulding. The product is available in natural but other colours can be provided on request DFR210 is especially designed for technical parts. In addition to having good flame retardant properties this product has an extremely low level of toxicity in case of fire. DFR210 is mainly intended for the injection moulding of electrical components (conform 2002/95/EC, RoHS directive). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.74 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4200 | MPa | ISO 178 |
| Flexural Stress | 112 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 36 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | ISO 4589-2 | ||
| -- 2 | 31 | % | ISO 4589-2 |
| -- 3 | 35 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 1.6 mm |
| 3 . | 3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Verolloy S3500 | PlastxWorld Inc. | PC+ABS | Verolloy |
| Zythane® 4050D | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Clariant Nylon 6/6 66G25M15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Deco-Coat™ UV Cure 7155™ | Epoxies, Etc. | Epoxy | Deco-Coat™ |
| EVALENE® PP PRB0202 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |