NYCOA Polyamide 2610
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XnfyZY_NYCOA-Polyamide-2610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2610 is a low viscosity Nylon 6/12 that features excellent dimensional stability, with low moisture absorption. This grade is available in custom viscosities, and additive packages. Typical applications include monofilament, tubing, and structural injection molded parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 62.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 2050 | MPa | ASTM D790 |
| Flexural Strength 4 | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 155 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 58.3 | °C | ASTM D648 |
| Melting Temperature | 217 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789.Tensile Elongation at Break, ASTM D638, 2 in/min: 300+% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 243 - 254 | °C | |
| Nozzle Temperature | 243 - 254 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 65.6 - 76.7 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 20YM240 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| Rotec® ABS SE 3 HH | ROMIRA GmbH | ABS | Rotec® ABS |
| ALCOM® POM 770/1 SLBV | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| Diaterm® A27 SSR GF30 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |
| Daelim Po1y® VL0005 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |