Elastollan® 1190 A 10 FHF 000
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xn4DPM_Elastollan-1190-A-10-FHF-000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen-free flame retardant, thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 90 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 30.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% Strain | 5.00 | MPa | |
| 100% Strain | 8.00 | MPa | |
| 300% Strain | 11.0 | MPa | |
| Tensile Stress | DIN 53504-S2 | ||
| Yield 1 | 15.0 | MPa | |
| Yield | 25.0 | MPa | |
| Tensile Elongation | DIN 53504-S2 | ||
| Break 2 | 640 | % | |
| Break | 550 | % | |
| Tear Strength 3 | 60 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 26 | % | |
| 70°C, 24 hr | 43 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 46 | kJ/m² | |
| 23°C | No Break |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 | °C | |
| Rear Temperature | 205 to 215 | °C | |
| Middle Temperature | 210 to 225 | °C | |
| Front Temperature | 215 to 225 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 215 to 225 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 to 15.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 160 to 180 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 190 to 210 | °C | |
| Cylinder Zone 4 Temp. | 200 to 220 | °C | |
| Adapter Temperature | 200 to 220 | °C | |
| Die Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water at 80°C for 42 days |
| 2 . | after storage in water at 80°C for 42 days |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (PC) XP 41 R 10 GF | A. Schulman Europe | PC | POLYMAN® |
| 4MID® 9AB22120 HUV2 | 4Plas | Nylon 66/6 | 4MID® |
| Altuglas® BS 510 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| LIM™ 6030 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | LIM™ |
| Karina RED PVC COMPOUND -E 870-42/179-A-IS (C850) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |