Badamid® LB70 GF20 FR HF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XmwhkZ_Badamid-LB70-GF20-FR-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LB70 GF20 FR HF is a Polyamide 6 (Nylon 6) material filled with 20% glass fiber. It is available in Europe. Primary attribute of Badamid® LB70 GF20 FR HF: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.31 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 95.0 | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | 6.0 | % | ISO 527-2/5 |
| Flexural Stress (23°C) | 150 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 3.0 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 40 | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 10 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 170 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 222 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 5.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.5E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 60216 | |||
| -- 2 | 160 | -- | °C | |
| -- | 180 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+11 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| Glow Wire Flammability Index (0.750 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 20000 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NG40-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Fibremod™ GD301FE | Borealis AG | PP, Unspecified | Fibremod™ |
| Kemcor MD 0898 | Qenos Pty Ltd | MDPE | Kemcor |
| Karina WHITE PVC COMPOUND 833D10/184-AY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ KL001 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |