UNIPA® lm

Category:	Nylon 612 , Polyamide 612
Manufacturer:	Nytef Plastics, Ltd.
Trademark:	UNIPA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XmvWW6_UNIPA-lm.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Since its introduction in 1938, Nylon has become one of the world's most widely recognized and utilized engineering grade thermoplastics. Nylon's unique combination of high strength, good toughness, outstanding chemical resistance, and excellent wear and abrasion resistance have made it the material of choice for product designs in a multitude of industries. When used to replace wear grade metals like brass and bronze, no other material provides the combination of extended wear life, light weight, and low fabricated part cost of Nylon. Nytef Plastics, Ltd. manufactures UNIPA® Nylon stock shapes in a wide variety of types and stock shape configurations. These UNIPA Nylon products fall into the categories of Type 6/6 Extruded UNIPA Nylons and Type 6 UNIPA M Cast Nylons. While both types of Nylon are very similar, there are performance and availability differences between the two
grades that should be noted:

UNIPA Type 6/6 Extruded Nylons:

offer improved toughness

offer improved flame resistance

are available in smaller rod diameters (< 2" dia.)

Nytef Plastic's UNIPA Nylon 6/6 extruded stock shapes are available in a wide range of grades— including both lubricated and fiber reinforced products. UNIPA Nylon 6/6 materials are offered in a complete range of extruded round, square, and hex rod, heavy gauge plate, and tubular bar sizes.

General Information
Features	Flame Retardant Good Abrasion Resistance Good Chemical Resistance Good Toughness Good Wear Resistance High Impact Resistance High Stiffness High Strength Low Moisture Absorption Machinable
Uses	Automotive Applications Bearings Bushings Construction Applications Electrical Parts Electrical/Electronic Applications Fluid Handling Food Service Applications Gears Mining Applications Molds/Dies/Tools Pulleys Pump Parts Rollers Textile Applications Valves/Valve Parts Wear Strip Wheels
Forms	Preformed Parts Rod

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.06	g/cm³	ASTM D792
Water Absorption			ASTM D570
24 hr	0.25	%
Saturation	3.0	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	108		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2240	MPa	ASTM D638
Tensile Strength	55.2	MPa	ASTM D638
Tensile Elongation (Break)	200	%	ASTM D638
Flexural Modulus	2070	MPa	ASTM D790
Flexural Strength	96.5	MPa	ASTM D790
Compressive Strength	107	MPa	ASTM D695
Coefficient of Friction	0.30		ASTM D1894

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	64	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	65.0	°C	ASTM D648
Continuous Use Temperature	93.3	°C	Internal Method
Peak Melting Temperature	217	°C	ASTM D3418
CLTE - Flow	9.0E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+13	ohms·cm	ASTM D257
Dielectric Constant			ASTM D150
1 MHz	4.00
60 MHz	6.00
Dissipation Factor (60 Hz)	0.15		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating	HB		UL 94

Resin Grade	Manufacturer	Category	Trademark
Salflex 925	Salflex Polymers Ltd.	HDPE	Salflex
SNOLEN® IM 13/56 S	JSC Gazprom neftekhim Salavat	HDPE	SNOLEN®
WPP PP PPC6CF-1-Black	Washington Penn Plastic Co. Inc.	PP Copolymer	WPP PP
Elastron® V P.V101.A65.B	Elastron USA, Inc.	TPV	Elastron® V
ExxonMobil™ HDPE HPA 020HD5 Molding	ExxonMobil Chemical	HDPE, HMW	ExxonMobil™ HDPE