ACCUCOMP™ CP0402V
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xmq3aW_ACCUCOMP-CP0402V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ CP0402V is a Polypropylene Copolymer (PP Copolymer) product. It can be processed by extrusion and is available in North America. Typical application: Automotive. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 680 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 350 | % | ASTM D638 |
| Flexural Modulus | 680 | MPa | ASTM D790 |
| Flexural Strength | 30.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 62.0 | °C | |
| 1.8 MPa, Unannealed | 48.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 513 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| YUPLENE® H231P | SK Global Chemical | PP Homopolymer | YUPLENE® |
| NuSil MED-4960 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| Alathon® M6061 | LyondellBasell Industries | HDPE | Alathon® |
| ETILINAS HD5226AA | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |