LNP™ COLORCOMP™ 420C compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XmVKx2_LNPCOLORCOMP420Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* 420C is a compound based on PBT resin containing 30% glass. Added features of this grade include: excellent strength, stiffness and dimensional stability, high heat resistance. Good for appliance handles, spotlights, electric motors, connectors. Also known as: LNP* COLORCOMP* Compound 420 Product reorder name: 420C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Specific Volume | 0.660 | cm³/g | ASTM D792 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 30 | % | ASTM D229 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.30 - 0.50 | % | Internal method |
| Flow 2 | 0.50 - 0.80 | % | Internal method |
| Flow 3 | 0.30 - 0.70 | % | Internal method |
| Flow : 3.20mm | 0.30 - 0.80 | % | Internal method |
| Transverse flow 4 | 0.40 - 0.60 | % | Internal method |
| Transverse flow 5 | 0.60 - 0.90 | % | Internal method |
| Transverse flow 6 | 0.50 - 1.0 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 1.0 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 122 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 7 | 9300 | MPa | ASTM D638 |
| -- | 9300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 8 | 120 | MPa | ASTM D638 |
| Yield | 125 | MPa | ISO 527-2/5 |
| Fracture 9 | 120 | MPa | ASTM D638 |
| Fracture | 125 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 10 | 2.7 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 11 | 2.7 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 12 | 7580 | MPa | ASTM D790 |
| -- 13 | 8500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 195 | MPa | ISO 178 |
| Yield, 50.0mm span 14 | 195 | MPa | ASTM D790 |
| Fracture, 50.0mm span 15 | 190 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 19.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 16 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 17 | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 80 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 18 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 19 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D4812 |
| -30°C 20 | 45 | kJ/m² | ISO 180/1U |
| 23°C 21 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 8.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 220 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 216 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 22 | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 203 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 207 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 23 | 204 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 24 |
| -- | 223 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 60 to 138°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Thermal Conductivity | 0.19 | W/m/K | ISO 8302 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | > 3.2E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 1.60 mm, in Oil | 25 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 19 | kV/mm | ASTM D149 |
| 0.800mm, in oil | 28 | kV/mm | IEC 60243-1 |
| 1.00 mm 25 | 19 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 24 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 100 Hz | 3.80 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 | |
| 50 Hz | 3.10 | IEC 60250 | |
| 60 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | |||
| 100 Hz | 2.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 100 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Arc Resistance 26 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 19 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 66 - 88 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | Tensile Bar |
| 4 . | 1.5 to 3.2 mm |
| 5 . | 3.2-4.6 mm |
| 6 . | Tensile Bar |
| 7 . | 5.0 mm/min |
| 8 . | Type 1, 5.0 mm/min |
| 9 . | Type 1, 5.0 mm/min |
| 10 . | Type 1, 5.0 mm/min |
| 11 . | Type 1, 5.0 mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | 1.3 mm/min |
| 15 . | 1.3 mm/min |
| 16 . | 80*10*4 sp=62mm |
| 17 . | 80*10*4 sp=62mm |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 80*10*4 |
| 22 . | 80*10*4 mm |
| 23 . | 80*10*4 mm |
| 24 . | 标准 B (120°C/h), 载荷2 (50N) |
| 25 . | Short-Time |
| 26 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1378 CL Black | RTP Company | PPS | RTP |
| Telcar® TL-2570A | Teknor Apex Company | TPE | Telcar® |
| Cellophane™ 335WSZB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Loyblend® TA-1100 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| NYLOY® KF-0030N 311WT | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |