Durepol® PBT A3 G10 PRTA011 BT313 MSP
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XmPPim_Durepol-PBT-A3-G10-PRTA011-BT313-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyester PBT reinforced with 10% glass fiber in black, excellent mechanical and thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.70 to 1.2 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Ash Content | 8.0 to 12 | % | MAPM C-05 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.8 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 4000 | MPa | |
| 1000 hr | 2500 | MPa | |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 215 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 215 | °C | ISO 306 |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | ||
| 1.00 mm, 50 Hz | 2.0E-3 | ||
| 1.00 mm, 100 Hz | 2.0E-3 | ||
| 1.00 mm, 1 MHz | 0.020 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-315 (Roto) | Ravago Manufacturing Americas, LLC | HDPE | Ravago Compounds |
| SOLARENE DH200 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Axiall PVC 54915 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Ferro PP TPP20AN01NA NATURAL | Ferro Corporation | PP, Unspecified | Ferro PP |
| Pibifor® K2 GB/30 NATURALE | SO.F.TER. SPA | PBT | Pibifor® |