Bio-Flex® F 2110
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xm8po2_Bio-Flex-F-2110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bio-Flex ® F 2110 (prev. Bio-Flex® 467F) Biodegradable compound for film extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Apparent Density | 0.77 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 - 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 3.00 - 4.00 | cm³/10min | ISO 1133 |
| Moisture (30.0 µm) | 130 | g/m²/24 hr | ISO 15106-3 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | No Break | ISO 178 | |
| Tensile fracture strength | No Break | ISO 527 | |
| Tensile fracture strain | No Break | ISO 527 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (30.0 µm) | 1500 | cm³/m²/bar/24 hr | ISO 15105-2 |
| Nitrogen Permeability (30.0 µm) | 230 | cm³/m²/bar/24 hr | DIN 53380-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 730 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | > 300 | % | ISO 527-2 |
| Flexural Modulus | 680 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 17.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 83 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 78.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 145 - 160 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.30 | % | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 175 | °C | |
| Adapter Temperature | 175 | °C | |
| Melt Temperature | < 190 | °C | |
| Die Temperature | 175 | °C |
| Extrusion instructions |
|---|
| Water jacket (feed): 35 °CDie gap: 0.8 - 1.4 mmDie diameter: up to 400 mmBlow film ratio: 2.5 - 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5335 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| Sicoklar E81.15 | Ravago Group | PC | Sicoklar |
| Fainplast PVC PK 7015/UV | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Polimid A 30 GF | Poliblend S.p.a. | Nylon 66 | Polimid A |
| Sylvin 8309-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |