Order Products : sales@su-jiao.com
NYCOA Polyamide 5114
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XlSHIn_NYCOA-Polyamide-5114.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 5114 is a 14% glass fiber reinforced, impact modified, Nylon 66 that offers an excellent balance of mechanical properties. This grade features a higher degree of impact strength vs. traditional glassfilled Nylons. NYCOA 5114 is suitable for injection molding and can be found in applications in the hardware, and automotive industries. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 100 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus 3 | 3600 | MPa | ASTM D790 |
| Flexural Strength 4 | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 248 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 222 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 5005N-EE | TSRC Corporation | TPE | T-Blend® |
| VITAMIDE® BW34BK6358 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| ELITE™ 5538G | The Dow Chemical Company | EPE | ELITE™ |
| Hapflex™ 781 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| KOPHOS® KO1355H | Kolon Plastics, Inc. | PC | KOPHOS® |