BESTNYL SI00VI01BN-1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XlBmmg_BESTNYL-SI00VI01BN-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 Standard, lubrified and fast cycle to achieve a faster injection and pieces moulding. Regularly used in small injection pieces and various cavities that requires a fast injection cycle. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 2.0 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 79 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3050 | MPa | ISO 527-2 |
| Tensile Stress | 72.0 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 225 to 240 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GTPO9005 | S&E Specialty Polymers, LLC | TPO (POE) | S&E Wire & Cable |
| S&E Footwear GF-3161PNU | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Footwear |
| Keltan® 5465Q | LANXESS Buna GmbH | EPDM | Keltan® |
| Karina WHITE PVC COMPOUND 802D10/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| XYLEX™ HX8300HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |