CALIBRE™ 303V-15
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xl3Tlg_CALIBRE-303V-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 300V-15 Series polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. The CALIBRE 300V series products are available in 2 additive packages: CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mold release and UV stabilizer. Govt. And Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 71.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress 2 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 850 | J/m | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 121 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 137 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 805C | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| RheTech Polypropylene M40P200-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| TAIRIPRO B8001 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Borstar® ME6053 | Borealis AG | MDPE | Borstar® |
| Sylvin 5170-85 Blue 8323 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |