POLYMAN® (ABS) LP 299/2 GL
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYMAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xl1ngR_POLYMAN-ABS-LP-299-2-GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium impact ABS grade |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 21.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 104 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.4 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 87.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 74.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 96.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 36 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 650 | °C | |
| 3.00 mm | 650 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 675 | °C | |
| 3.00 mm | 675 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 216 V30 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| BESTNYL SE35VI02AX | Triesa Plastics | Nylon 66 | BESTNYL |
| Karina WHITE PVC COMPOUND 800-10/93-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| COSMOPLENE® AX161S | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| Kinta FR5000-J001 | Kinta Technology (Hong Kong) Co., Ltd. | PC | Kinta |