PALPROP® R C 25

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	pal plast GmbH
Trademark:	PALPROP®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XkGq7R_PALPROP-R-C-25.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALPROP®R C 25 is a polypropylene impact copolymer (PP Impact Copoly) product,. It can be processed by injection molding and is available in Europe. PALPROP®R C 25 applications include packaging, the automotive industry and consumer goods. Features include: Impact resistance High stiffness Copolymer

General Information
Features	Block Copolymer Rigidity, high Impact resistance, high Good liquidity Low temperature impact resistance
Uses	Packaging Leather case Application in Automobile Field
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.910	g/cm³	ISO 1183

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	1300	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	26.5	MPa	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	18	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.5	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	68.0	°C	ISO 306/B50

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1200 to 1400 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 25 to 28 MPaNominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 15 to 20 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 7 to 10 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 66 to 70 °CDensity, ISO 1183: 0.9 to 0.92 g/cm³

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1200 to 1400 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 25 to 28 MPaNominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 15 to 20 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 7 to 10 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 66 to 70 °CDensity, ISO 1183: 0.9 to 0.92 g/cm³

Resin Grade	Manufacturer	Category	Trademark
Premier PI200	Premier Polymers, LLC.	PP Impact Copolymer	Premier
Sylvin 7821-55 BLACK	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Addisil™ 6200	Momentive Performance Materials Inc.	Silicone	Addisil™
EPO-TEK® H22	Epoxy Technology Inc.	Epoxy	EPO-TEK®
Axiall PVC 1651	Axiall Corporation	PVC, Flexible	Axiall PVC