VITAMIDE® AS30NT6001
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XkEUx4_VITAMIDE-AS30NT6001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AS30NT6001 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 74.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 55 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Break | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 10.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 27 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | > 530 | V | IEC 60112 |
| -- 2 | > 530 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S USX200 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Michilene F8200-03 | API Polymers, Inc. | PP Copolymer | Michilene |
| Ultrathene® UE637000 | LyondellBasell Industries | EVA | Ultrathene® |
| Elvaloy® AC 3717 | DuPont Packaging & Industrial Polymers | EnBA | Elvaloy® |
| LEXAN™ HFD1262 resin | SABIC Innovative Plastics | PC | LEXAN™ |