| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XiyzPd_SUPREME-PP-SPEXP49.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Characteristics:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 40 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 2230 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 43.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 26 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 155 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 260 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 180 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKAEXCEL® PES 4101GL30 | Sumitomo Chemical Co., Ltd. | PESU | SUMIKAEXCEL® PES |
| WPP PP UP4I203 - Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Garaflex™ E 4362-A1 NAT LCF | AlphaGary | TPE | Garaflex™ E |
| PHOENIX™ 8301 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| OTECH ALLOY OE5115 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |