Badadur® PBT8 GF30 TM-Z2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XhTG0n_Badadur-PBT8-GF30-TM-Z2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, 30 % GF reinforced injection moulding grade with very good mechanical properties, high toughness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.49 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.13 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break) | 4.5 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength 6 | ISO 179/1eU | ||
| -30°C | 70 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Notched Izod Impact Strength 7 | |||
| -30°C | 11 | kJ/m² | ISO 180 |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 9 | 223 | °C | ISO 3146 |
| CLTE 10 | DIN 53752 | ||
| Flow | 3.5E-5 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | ||
| 20000 hrs | 135 | °C | |
| some hours | 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 12 | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength 13 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity 14(1 MHz) | 4.00 | IEC 60250 | |
| Dissipation Factor 15(1 MHz) | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm 16 | HB | ||
| 1.60 mm 17 | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 110x10x4 mm |
| 9 . | 10 K/min, Compound for moulding |
| 10 . | >=10x10x4 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 80x80x1 mm |
| 16 . | 125x13x0.8 |
| 17 . | 125x13x1.6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lumicene® M 6012 EP | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| ADENE NCZAG | A.D. Compound spa | PP Copolymer | ADENE |
| ALKAMIX™ MB-UV815 | Marplex Australia Pty. Ltd. | PE, Unspecified | ALKAMIX™ |
| ETILINAS LL0209SA | POLYETHYLENE MALAYSIA SDN BHD | LLDPE | ETILINAS |
| Expandable PS F11MB | INEOS Styrenics International SA | PS (EPS) | Expandable PS |