Di-Pak™ R-4260
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XgnbH1_Di-Pak-R-4260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4912 & R-4260 A/B Low viscosity, fast cure, high performance, high HDT potting and encapsulating compounds with excellent properties and FAST TURNOVER. Both are two part systems with 1:1 mix ratios by volume. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D2566 |
| Weight - per cubic inch | 18 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 146 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 655 | MPa | ASTM D638 |
| Tensile Strength | 53.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 1820 | MPa | ASTM D790 |
| Flexural Strength | 73.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 9.6 | J/m | ASTM D256 |
| Unnotched Izod Impact | 56 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.7E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.73 | ||
| 100 kHz | 3.50 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.22 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 86, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 600 | cP | ASTM D4878 |
| Demold Time (21°C) | 5.0 to 12 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7821-78 LMW BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen EP540V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Flontech® FT-GL25-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Capilene® CT 71 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| Hylon® N1035STHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |