PROTEQ™ C16UST4
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XgP3SF_PROTEQ-C16UST4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C16UST4 medium melt flow automotive polypropylene copolymer containing 20% talc filler which features improved heat ageing and UV performance. PROTEQ™ C16UST4 has been designed to meet the stringent requirements of automotive interior trim durabilty specifications, combining easy processing with reduced gloss and improved marr resistance. Typical automotive interior applications are consoles, seat bolsters, steering shrouds, door liners and glovebox lids. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 72 | ||
| Shore D, 15 sec | 63 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 47.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 60 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 | °C | |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Semitron® ESd 225 | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| SUPREME Specialty PS SP266 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| NEMCON H PA DP117/X3 | Ovation Polymers Inc. | PEEK | NEMCON H |
| Fainplast PVC FKT 92 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| OTECH CPE XLO9141 - Cable Jacket | OTECH Corporation | CPE | OTECH CPE |