ACCUCOMP™ HD0200L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XgNG4Q_ACCUCOMP-HD0200L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ HD0200L is a High Density Polyethylene product. It is available in North America. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 33 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 950 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 26.0 | MPa | |
| Break | 15.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 44 | % | |
| Break | 350 | % | |
| Flexural Modulus | 800 | MPa | ASTM D790 |
| Flexural Strength | 21.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 62.0 | °C | |
| 1.8 MPa, Unannealed | 43.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 815CI | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Cheng Yu FV30715 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| ColorRx® PC-0700RX | LTL Color Compounders, Inc. | PC | ColorRx® |
| DI-COAT R-4721LV/30 | Hapco Inc. | TP, Unspecified | DI-COAT |
| StarFlex® 7360-9000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |