Fortron® 6345L4
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XfIgA8_Fortron-6345L4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 6345L4 is 30% glass fiber/high PTFE reinforced injection molding grade. This grade, available in natural and black color, exhibits improved wear and sliding properties versus 1342L4 product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.60 - 0.90 | % | ISO 294-4 |
| Flow direction | 0.30 - 0.50 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic 1 | 0.28 | ASTM D1894 | |
| Dynamic 2 | 0.28 | ASTM D1894 | |
| Static 3 | 0.30 | ASTM D1894 | |
| Static 4 | 0.29 | ASTM D1894 | |
| With steel-dynamic 5 | 0.15 | ASTM D1894 | |
| With steel-static 6 | 0.17 | ASTM D1894 | |
| Wear Factor 7 | ASTM D3702 | ||
| 416 Stainless : 32°C | 148 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 49°C | 120 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| C-1018 Steel : 93°C | 415 | 10^-10 in³·min/ft·lb·hr | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 190 | °C | ISO 75-2/C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | vs Fortron 1140L4, 73°F, 5 lbf, 5 in |
| 2 . | vs Fortron 6165A4, 73°F, 5 lbf, 5 in |
| 3 . | vs Fortron 6165A4, 73°F, 5 lbf, 5 in |
| 4 . | vs Fortron 1140L4, 73°F, 5 lbf, 5 in |
| 5 . | 73°F, 5 lbf, 5 in |
| 6 . | 73°F, 5 lbf, 5 in |
| 7 . | 16 µ-in, PV2000, 40 psi, 50ft/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® PR40 LHS | Nilit Plastics | Nylon 66 | POLYNIL® |
| RTP 209 Z | RTP Company | Nylon 66 | RTP |
| AVP™ FLLS0CP | SABIC Innovative Plastics | PC | AVP™ |
| Hipolyene 8515 TY | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Moplen EP200R | PolyMirae | PP Impact Copolymer | Moplen |