AVP™ GLT25CP
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XeOWBQ_AVP-GLT25CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AVP™ GLT25CP is a Polycarbonate + PET (PC+PET) product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 56.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 110 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 116 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL EXC NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 254 to 268 | °C | |
| Middle Temperature | 254 to 268 | °C | |
| Front Temperature | 260 to 274 | °C | |
| Nozzle Temperature | 254 to 268 | °C | |
| Processing (Melt) Temp | 266 to 279 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa | |
| Screw Speed | 25 to 50 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-133G13 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Hostacom LPX 1702 100015 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Jackdaw PP EV18BN6467 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| Karina IVORY PVC COMPOUND -E 630D35/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 5145-70 Clear Red 6202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |