REPOL® H110FU
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xe9b3l_REPOLH110FU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol H110FU is recommended for Staple Fibres & Continuous High Tenacity Filaments. The grade is specially formulated for Anti gas fading and UV stability. Repol H110FU is an ideal material for spinning of fine denier staple fibres. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 8.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Injection Molded) | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Injection Molded) | 104 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1910 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| ALCOM® TCD PA66 5030 14014 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® TCD PA66 |
| Epoxies, Ect. 10-3020 NS | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| KumhoSunny PC/ABS HAC8245 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Polygen SG6R | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |