RTV-2 XP-614
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xe7zD1_RTV-2-XP-614.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XP-614 is a fast curing, two-component addition cure silicone rubber mold making material that has a minimum working time of 40 minutes, yet can be demolded in only 3 to 4 hours. This allows the mold maker to produce both sides of a two part mold in one 8 hour shift. Parts can also be produced in the same day from a one piece mold. XP-614 also has a high durometer, minimal shrinkage and excellent chemical resistance, making it a superior choice for prototyping and casting solid polyurethane resins. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity 1 | 1.24 | g/cm³ |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity | 35000 to 45000 | cP | ASTM D2393 |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Black | ||
| -- 3 | Grey | ||
| -- 4 | Tan | ||
| Viscosity | |||
| -- 5 | 0.80 to 1.2 | Pa·s | |
| -- 6 | 45 to 55 | Pa·s | |
| Curing Time | 4.0 | hr | |
| Pot Life | > 40 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 7 | > 34 | ||
| Shore A 8 | 50 to 60 | ||
| Shore A 9 | 55 to 65 | ||
| Tensile Strength | 3.79 to 4.48 | MPa | |
| Tensile Elongation at Break | 150 to 200 | % | |
| Tear Strength | 6.13 to 9.63 | kN/m |
| Note Message | |
|---|---|
| 1 . | Cured |
| 2 . | Activator |
| 3 . | Mixed |
| 4 . | Base |
| 5 . | Activator |
| 6 . | Base |
| 7 . | 4 Hours |
| 8 . | 18 Hours |
| 9 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A70 G30 U NC284 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| DJSilicone NE-Z260 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Lotrène® LDPE FE8004 | QAPCO | LDPE | Lotrène® LDPE |
| Westlake LDPE EF310 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Elastoprene S1075A | KMI Group, Inc. | TES | Elastoprene |