Ultrason® S 6010
| Category: | PSU , Polysulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XdgLct_Ultrason-S-6010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultrason S 6010 is a high molecular weight injection molding and extrusion grade with excellent chemical resistance (stress crack resistance) and good solubility in typical solvents (N-methylpyrrolidone, dimethlyacetamide, dicholormethane) used in the production of membranes or coatings. Applications Typical applications include sanitary and heating systems/parts and membranes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.77 | % | |
| Flow | 0.72 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2550 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.7 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.5 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 6.5 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 177 | °C | ISO 75-2/A |
| CLTE - Flow | 5.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.50 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.1E-3 | ||
| 1 MHz | 7.1E-3 | ||
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 340 to 390 | °C | |
| Mold Temperature | 140 to 180 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® 100 | ITEN INDUSTRIES | Phenolic | Resiten® |
| Sinpolene MBW009 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Axiall PVC 10703 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Fainplast PVC CRKA 01227 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 3280-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |