RTP 107 HS UV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xd2B0t_RTP-107-HS-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10300 | MPa | ASTM D638 |
| Tensile Strength | 57.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 6550 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 240 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 166 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, ASTM D-955, 0.25in.: 4mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 218 - 274 | °C | |
| Middle Temperature | 218 - 274 | °C | |
| Front Temperature | 218 - 274 | °C | |
| Mold Temperature | 32.2 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 6019 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Random Copolymer | POLYPRO® |
| Rhelon G2930H-00 | RheTech, Inc. | Nylon 66 | Rhelon |
| Starex GR-4015A | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Nylene® 4114-33 GL HS | Custom Resins Group | Nylon 66 | Nylene® |
| LEXAN™ HFD1433 resin | SABIC Innovative Plastics | PC | LEXAN™ |