AKROMID® B3 GF 15 S1 black (1270)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xcx1gU_AKROMID-B3-GF-15-S1-black-1270-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 15 S1 black (1270) is a 15% glass fibre reinforced, cold impact strength polyamide 6 with medium stiffness and strength Applications are highly integrated housings in the automotive, electro and furniture industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.22 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Humidity Absorption - 62% RH (70°C) | 2.3 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 15 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5800 | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 115 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | 10 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 190 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 45 | kJ/m² | |
| 23°C | 70 | 95 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 HB | RTP Company | Nylon 66 | RTP |
| Royalene® 301T | Lion Copolymer, LLC | EPDM | Royalene® |
| Karina BLACK PVC COMPOUND 807D48/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Stat-Tech™ PA66 C20 black (EM00000364BI) | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| Sylvin 9067-90 Blue 8232 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |