LUBEMID B27 GF30 FR V0 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XcsAVp_LUBEMID-B27-GF30-FR-V0-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6 first choice natural colour. With glass fibres 30%. UL 94 V0 classified. With halogens. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 to 1.58 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7700 to 8200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 115 to 125 | MPa | |
| Break | 115 to 125 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 1.5 to 2.0 | % | |
| Break | 1.5 to 2.0 | % | |
| Flexural Modulus 1 | 7200 to 7700 | MPa | ISO 178 |
| Flexural Stress 2 | 150 to 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 to 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 to 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 65 to 75 | J/m | ASTM D256A |
| 23°C 3 | 60 to 70 | kJ/m² | ASTM D256 |
| 23°C | 6.0 to 7.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 6.5 to 7.5 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 60 to 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 210 to 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 215 to 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 190 to 200 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 200 to 210 | °C | ISO 306/A120 |
| -- | 190 to 200 | °C | ISO 306/B120 |
| Melting Temperature | 210 to 225 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1910 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| VITAMIDE® AY15 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| TOTAL Polyethylene HDPE XT10B | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| CYCOLOY™ EX58 resin | SABIC Innovative Plastics Asia Pacific | ABS | CYCOLOY™ |
| KumhoSunny PC/ABS HAC8250 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |