PENTAMID A E20 H schwarz
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XbpyLE_PENTAMID-A-E20-H-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, high impact modified, heat stabilised polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.6 | -- | % | ISO 294-4 |
| Flow direction | 1.4 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.2 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 100 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 45.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 7.0 | 35 | % | ISO 527-2 |
| Fracture | 40 | 50 | % | ISO 527-2 |
| Flexural Modulus | 1750 | -- | MPa | ISO 178 |
| Flexural Stress | 70.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 17 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 75 | 100 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.20 | -- | IEC 60250 | |
| Comparative Tracking Index | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA66-HI, MHRC, 14-020 NThe value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >40% |
| 调节后的 ISO Description: PA66-HI, MHRC, 14-020 NTensile Strain at Break, ISO 527: >50%Unnotched Charpy Impact, ISO 179, 23°C, Type 1, Edgewise: >100 kJ/m² |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.14 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 260 - 285 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 65.0 | MPa | |
| Holding Pressure | 39.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terblend® N NG-06 | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| Baoding 6126 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Halene H R5801 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| OTECH PVC OW134 - Automotive Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Maxxam™ PP5140F A7 | PolyOne Corporation | PP Homopolymer | Maxxam™ |