Pharmalene® FL 20 PH
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Pharmalene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XaS1SG_Pharmalene-FL-20-PH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pharmalene FL 20 PH is a homopolymer low density polyethylene (LDPE) without additives obtained by high pressure autoclave process. It is manufactured according to good manufacturing practices (GMP). The main use is in the pharmaceutical sector. Pharmalene FL 20 PH has high swell and good melt strength. It is suitable for injection blow moulding of single-use small containers. The polymer can be used in film. Extruded films are easily heat shrinkable and have good optical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 28 - 80 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 40 µm, Blown Film | 160 | MPa | |
| 1% Secant, TD : 40 µm, Blown Film | 180 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 10.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 19.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 300 | % | |
| TD : Break, 40 µm, Blown Film | 550 | % | |
| Dart Drop Impact 1(40 µm, Blown Film) | 190 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, Blown Film | 70 | N | |
| TD : 40 µm, Blown Film | 45 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A |
| Melting Temperature | 109 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 54 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 9.0 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 160 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 132.2 | RTP Company | PP Homopolymer | RTP |
| TERPOL® ABS | EMAS Plastik San.Tic.AS. | ABS | TERPOL® |
| Abstron IMC45V | Bhansali Engineering Polymers Limited | PC+ABS | Abstron |
| Kingfa API-2500 | Kingfa | PP, Unspecified | Kingfa |
| LEXAN™ GLX143 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |