TUFNYL® RHS NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SRF Ltd. |
| Trademark: | TUFNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XaIruI_TUFNYL-RHS-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, Un-Filled heat stabilized material for injection molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 to 1.8 | % | Internal Method |
| Water Absorption (Equilibrium) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 80 | ||
| R-Scale | 115 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 49.0 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 260 | °C | DSC |
| Heat Stability | ASTM D4066 | ||
| 24 hrs : 204°C | Passes | ||
| 72 hrs : 204°C | Passes |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP110-13-45 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Triax® 1120 | INEOS Styrolution Group GmbH | ABS+Nylon | Triax® |
| Axplas® r-PP51 0000 | Axion Polymers | PP, Unspecified | Axplas® |
| Karina CLEAR PVC COMPOUND -E 80/214-SD-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DFL32P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |