SABIC® LDPE 2404AN00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XZxxfc_SABIC-LDPE-2404AN00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® LDPE 2404AN00 is an autoclave grade without additives. The material can be easily processed with minimum smoke development. The material is characterised by an optimal relationship between draw down and neck-in and excellent adhesion to various substrates. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 2.00mm, molded | 11.0 | MPa | ISO 527-2/50 |
| Fracture, 2.00mm, molded | 14.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 640 | % | ISO 527-2/50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 10.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm | 9.00 | MPa | ISO 527-3 |
| MD : 25 µm | 14.0 | MPa | ISO 527-3 |
| TD : 25 µm | 13.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 300 | % | ISO 527-3 |
| TD : Break, 25 µm | 450 | % | ISO 527-3 |
| Oxygen Permeability (23°C, 25 µm, 0% RH) | 200 | cm³·mm/m²/atm/24 hr | ISO 15105-2 |
| Water Vapor Transmission Rate (38°C, 90% RH, 25 µm) | 18 | g/m²/24 hr | ISO 15106-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 111 | °C | DIN 53765 |
| Enthalpy Change | 124 | J/g | DIN 53765 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 6383-2 | ||
| MD : 25.0 µm | 12.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 9.0 | kN/m | ISO 6383-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM 5502LD | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| MAZMID B 150 FV 25 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Andur 7500 DP | Anderson Development Company | PUR-Ether/TDI | Andur |
| HAIPLEN H30 G8 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Sylvin 6250-82 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |