Hytrel® HTR8441 BK316
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XZPBxG_Hytrel-HTR8441-BK316.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55 Shore D High Viscosity Polyester Elastomer Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (240°C/10.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 2.1 | % | |
| Flow | 2.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 58 | ||
| Shore D, 15 sec | 52 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 190 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 35.0 | MPa | |
| 5.0% Strain | 7.80 | MPa | |
| 10% Strain | 11.9 | MPa | |
| 50% Strain | 19.0 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 380 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength - Flow | 140 | kN/m | ISO 34-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 20 | kJ/m² | |
| -30°C | 39 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -54.0 | °C | ISO 974 |
| Melting Temperature 1 | 211 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 42 | mm/min | ISO 3795 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.01 | g/cm³ | |
| Specific Heat Capacity of Melt | 2150 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1840P | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TAROMID A 280 G2 X0 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| TOTAL Polyethylene LDPE FE 8000 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Haysite Plastics H722 GPO-1 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| LNP™ STAT-KON™ KEL32 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ STAT-KON™ |