CALIBRE™ 603-2
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XYY6d2_CALIBRE-603-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 603-2 Resin is specially designed for extrusion of super heavy wall sheet and very complex profiles. This resin offers exceptional high melt strength for effective calibration of complex structures, and excellent surface quality. The resin is UV bulk stabilized, but for outdoor use, co-extrusion with a UV cap is needed. It is recommended to apply a 50 micron layer of CALIBRE™ 320UV. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 1.8 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 4.00 mm, Injection Molded | 2350 | MPa | ASTM D638 |
| 4.00 mm, Injection Molded | 2400 | MPa | ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield, 4.00 mm, Injection Molded | 63.0 | MPa | |
| Break, 4.00 mm, Injection Molded | 51.0 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield, 4.00 mm, Injection Molded | 6.3 | % | |
| Break, 4.00 mm, Injection Molded | 50 | % | |
| Flexural Modulus (4.00 mm, Injection Molded) | 2400 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| 4.00 mm, Injection Molded | 93.1 | MPa | ASTM D790 |
| 4.00 mm, Injection Molded | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 69 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 4.00 mm, Injection Molded) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 140 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 146 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2(1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound PHC22-20 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| SURFACEMASTER® 905 | Cytec Industries Inc. | Epoxy | SURFACEMASTER® |
| ULTEM™ VH1003 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| Bergadur™ IDES 243031 | PolyOne Corporation | PBT | Bergadur™ |
| Sylvin 4200-85 Green 3212 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |