| N66A is a general purpose unfilled injection moulding grade of nylon 66. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.5 - 2.0 | -- | % | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2800 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3000 | 900 | MPa | ISO 178 |
| Flexural Stress 2 | 90.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 5.0 kJ/m² | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | 195 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | 75.0 | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 18 | 12 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | 4.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | > 600 | > 600 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| Back Pressure: LowInjection Pressure: MediumNo drying is necessary unless the material has been exposed to air for longer than 3 hours. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | At conventional deflection |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E580 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Spartech Polycom M60450 | Spartech Polycom | PVC, Unspecified | Spartech |
| Tuf-Stif 2802 | Axiall Corporation | PVC, Rigid | Tuf-Stif |
| Celstran® PP-GF30-0501P10 | Celanese Corporation | PP, Unspecified | Celstran® |
| K-PU 7760 | Technovinyl Polymers India Ltd. | TPU, Unspecified | K-PU |