Badamid® LA70 K
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XY2sWL_Badamid-LA70-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL listed, easy flowing injection moulding grade with short cycle times for technical products with isolating properties |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.0 to 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 to 3.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 3000 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 85.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 5.0 | 20 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 5.0 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 5.5 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/B |
| Melting Temperature (DSC) 4 | 260 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 60216 | |||
| -- 5 | 118 | -- | °C | |
| -- | > 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.20 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/min |
| 5 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinylbond 95-950-65 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Clariant Nylon 6/6 6608-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Gallonprene® GP200-5 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Plaslube® PPS/F CF30 TL15 BK | Techmer Engineered Solutions | PPS | Plaslube® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 3712 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |