QAMAR HB18N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SPDC Ltd. |
| Trademark: | QAMAR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XXY2Y3_QAMAR-HB18N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
QAMAR HB18N is a linear low density polyethylene material,. This product is available in North America, Africa and the Middle East, Europe or Asia Pacific region. The processing method is blow molded film. The main characteristics of QAMAR HB18N are: high strength. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1872-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 9.00 | MPa | ISO 1872-2 |
| Tensile Strain (Break) | > 430 | % | ISO 1872-2 |
| Flexural Modulus | 200 | MPa | ISO 1872-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 30 µm | 200 | MPa | ISO 527-3 |
| TD : 30 µm | 230 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 30 µm | 60.0 | MPa | ISO 527-3 |
| TD : Break, 30 µm | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 30 µm | 500 | % | ISO 527-3 |
| TD : Break, 30 µm | 850 | % | ISO 527-3 |
| Dart Drop Impact (30 µm) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 30 µm | 30 | N | ISO 6383-2 |
| TD : 30 µm | 170 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ISO 974 |
| Vicat Softening Temperature | 102 | °C | ISO 306 |
| Melting Temperature | 122 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 7.0 | % | ISO 14782 |
| Extrusion instructions |
|---|
| Resin Temperature: 200°CBlow up Ratio: 2.0Extruder: 40 mm, L/D=24Die Diamteter: 75 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SV-14000U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Elexar® EL-8431 | Teknor Apex Company | TPE | Elexar® |
| Hanwha Total PP BI616 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| KOPA® KN133G33HIBK | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| StarPrene® 6101-61 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPrene® |