Clariant Nylon 6/6 R66G13-L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XXVgIA_Clariant-Nylon-6-6-R66G13-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clariant Nylon 6/6 R66G13-L is a Polyamide 66 (Nylon 66) material filled with 13% glass fiber. It is available in North America for injection molding. Primary attribute of Clariant Nylon 6/6 R66G13-L: Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Tensile Impact Strength | 11.3 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 249 | °C | |
| 1.8 MPa, Unannealed | 235 | °C | |
| Melting Temperature | 257 to 264 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 282 to 299 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Mold Temperature | 71.1 to 104 | °C | |
| Injection Pressure | 55.2 to 138 | MPa | |
| Back Pressure | 0.00 to 1.03 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PG-33 | CHI MEI CORPORATION | PS (GPPS) | POLYREX® |
| Unichem 8005 | Colorite Polymers | PVC, Unspecified | Unichem |
| Aurora PVC AP2261 | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Karina BLACK PVC COMPOUND 650-48/1-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® BM 29 X H2.0 EF 900116 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |